 note = {application/pdf, In this study, pure LaB6 ceramic powder was hot-pressed to prepare a sintered compact when the press pressure was changed from 7.05 to 28.17 MPa, and the mechanical and electrical properties were revealed.
The relative density improved in proportion to the press pressure, and 82.9-95.3% was obtained. When the hot-press pressure is 28.17MPa, the sintered compact has a relative density of 95.3%, Vickers hardness 15.2GPa, flexural strength 216MPa, fracture toughness 2.06MPa・m1 / 2, Young's modulus 204GPa, shear modulus 84.8 GPa, surface roughness Ra 297nm and electric conductivity 7.67MS/m. It is characterized by having high electrical conductivity.},
 pages = {1--8},
 title = {ホットプレスLaB₆セラミックスの機械的及び電気的特性},