| タイトル | Si3N4, AlN, SiCセラミックスのYAGレーザ－切断加工と機械的特性 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | YAG laser cutting of Si3N4, AlN, SiC ceramics and its mechanical property | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||
| 主題 | Si3N4 | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||
| 主題 | AlN | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||
| 主題 | SiC | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||
| 主題 | YAGレーザー切断加工 | |||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||
| 著者 |
堀口勝三
× 堀口勝三
× 森山実
× 三尾敦
|
|||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | Si3N4, AlN and SiC ceramics with a relative density of 96.5% or more were processed by YAG laser cutting, and the change in strength due to the processing was evaluated. When a single laser beam was irradiated, the beam depth ? increased in proportion to the energy E [J] of the laser beam. The relationship between E and ? is about 1J→0.6~0.8mm, 2J→0.9~1.1mm. The beam-hole diameter with conical shape was 0.15 to 0.22 mm at the irradiated surface. The Vickers hardness of the processed surface decreased to about 13-22%. The 3-point bending strength decreased to 33-45%. The surface roughness decreased greatly from 1/62 to 1/146. From the observation of the structure of the irradiated cross section, the structure melted by heat of laser beam was observed in Si3N4 and AlN, and the sintered structure with traces of processing was observed in SiC. |
|||||||||||||||||
| 言語 | en | |||||||||||||||||
| 書誌情報 |
巻 1, 号 2-02, 発行日 2024-08-30 |
|||||||||||||||||
| 出版者 | ||||||||||||||||||
| 出版者 | 長野工業高等専門学校 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 1882-9155 | |||||||||||||||||
| 書誌レコードID | ||||||||||||||||||
| 収録物識別子タイプ | NCID | |||||||||||||||||
| 収録物識別子 | AA1259397X | |||||||||||||||||
| 見出し | ||||||||||||||||||
| 大見出し | 研究報告 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||