 author = {長坂, 明彦 and 宮脇, 崇 and 押田, 京一 and 川村, 渉 and 柳澤, 憲史 and 百瀬, 成空},
 journal = {長野工業高等専門学校紀要, Memoirs of Nagano National College of Technology},
 month = {Jun},
 note = {Effect of Vapor Grown Carbon Fiber (VGCF) content on mechanical properties and abrasion resistance in Polytetrafluoroethylene (PTFE) -VGCF composite was investigated. The resin powder of PTFE was used as a matrix of 50 μm in diameter, and carbon nano material of VGCF was used as filler. Composite of PTFE resin and VGCF were mixed by blender mill. The VGCF addition was used from 0 wt% to 3 wt%. Tensile test was performed on an Instron type of tensile testing machine at a crosshead speed of 10 mm/min (strain rate: 6×10－3 /s), using smooth and V-notched type tensile specimens. Thermal conductivity (λ) was measured using laser flash method. Coefficient of dynamic friction (μ’) was measured using ball-on-disc method.},
 title = {PTFE-VGCFコンポジットの機械的性質および耐摩耗性に及ぼすVGCF添加率の影響},
 volume = {46},
 year = {2012}
}