@article{oai:nagano-nct.repo.nii.ac.jp:00000858,
 author = {森山, 実 and 板屋, 智之},
 journal = {長野工業高等専門学校紀要, Memoirs of Nagano National College of Technology},
 month = {Jun},
 note = {In this research, the sintered composite composed of WC ceramics and oriented 8vol%VGCF（vapor grown carbon nano-fiber）was prepared by hot-press method and its properties were investigated. The composite was prepared by sintering (under the condition of 1950°C×60min at press pressure of 26.3MPa in an Ar gas atmosphere) lined sodium alginate strings containing WC and VGCF, which obtained by injecting the slurry composed of WC, VGCF and sodium alginate into 30% HCl solution. Flexural strength and fracture toughness of the composite obtained by this process were slightly improved due to dispersed and oriented VGCF in the composite.},
 title = {CNFの配向処理とそのホットプレス焼結体の特性 : アルギン酸ナトリウムを用いた配向処理},
 volume = {48},
 year = {2014}
}